An InP/In/sub 0.53/Ga/sub 0.47/As resonant tunnelling bipolar transistor with double heterojunction grown by molecular beam epitaxy and fabricated by selective wet chemical etching is presented. An In/sub 0.53/Ga/sub 0.47/As/AlAs resonant tunnelling diode which achieves a current density of 15 kA/cm/sup 2 /at a peak voltage of 1.6 V for a peak-to-valley ratio of 39:1 is integrated at the emitter of a double heterojunction InGaAs/InP bipolar transistor. Results are presented for 3 /spl mu/m /spl times/ 3 /spl mu/m emitter size integrated device. A negative differential shape due to the resonant tunnelling effect at the emitter controlled by a 3.4 /spl mu/A base current is observed in the common-emitter current-voltage characteristics at room temperature with a current density of 9.2 kA/cm/sup 2 /and a peak-to-valley ratio of 12:1. The maximum current gain of the device is 220. However beyond the resonant tunnelling peak, the resonant tunnelling transistor presents a bistability where the collector current collapses dramatically, the transistor characteristics are recovered by increasing the collector-emitter voltage.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Design, fabrication and characterisation of an InP resonant tunneling bipolar transistor with double heterojunctions


    Beteiligte:


    Erscheinungsdatum :

    2002-01-01


    Format / Umfang :

    173811 byte





    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Electroluminescence properties of bipolar resonant tunneling diode [2321-36]

    Sheng, H. / Chua, S.-J. / Chinese Optical Society; Topical Committee on Optoelectronic Technology et al. | British Library Conference Proceedings | 1994


    On the InP/InGaAs Double Heterojunction Bipolar Transistor (DHBT) with Emitter Tunneling Barrier and Composite Collector Structure

    Chen, J. Y. / Lin, K. W. / Chen, C. Y. et al. | British Library Conference Proceedings | 2002