Outdoor exposure tests in marine atmosphere of 40CrNi2Si2MoVA high strength steel were carried out in Qingdao (on the east coast of Shandong facing the East China Sea) and Wanning (on the east coast of Hainan Island facing the South China Sea) respectively. The test samples include plate sample, samples for tensile and various stress corrosion cracking (SCC) test. The corrosion behavior of the steel was examined by means of mass loss measurement, SEM, as well as the change of mechanical property and SCC susceptibility. The results show that general corrosion occurs on the surface of 40CrNi2Si2MoVA steel, corrosion products are mainly Fe3O4, Fe2O3, γ-FeOOH and α-FeOOH; the mass losses vary at w=atb(b<1). The steel exhibited high SCC sensitivity in marine environment with typical intergranular cracking, and the crack initiated from corrosion pits in the surface and developed inwards. Higher corrosion rate and higher SCC sensitivity were observed in Hainan rather than in Qingdao. The decrease of tensile strength is result from corrosion inducing premature fracture in a short term.


    Access

    Access via TIB

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Marine Atmospheric Corrosion of 40CrNi2Si2MoVA High Strength Steel


    Additional title:

    Titel chinesisch


    Contributors:
    Zhang, Xiaoyun (author) / Liu, Ming (author) / Tang, Zhihui (author) / Liu, Minghui (author) / Sun, Zhihua (author)


    Publication date :

    2014


    Size :

    7 Seiten, Bilder, Tabellen, 15 Quellen



    Type of media :

    Article (Journal)


    Type of material :

    Print


    Language :

    Unknown




    CORROSION RESISTANT STEEL FOR MARINE AND MARINE

    OZAWA KEISUKE / KAWANO HARUYA / SAKASHITA SHINJI | European Patent Office | 2017

    Free access

    Atmospheric Corrosion Mechanisms of Painted Steel

    Standish, John V. | SAE Technical Papers | 1983


    HIGH STRENGTH SPRING STEEL HAVING EXCELLENT CORROSION RESISTANCE

    CHA SUNG CHUL / HONG SEUNG HYUN / KIM IK SOO et al. | European Patent Office | 2017

    Free access

    Corrosion resistance of high-strength modified 13 % Cr steel

    Kimura, M. / Miyata, Y. / Yamane, Y. et al. | Tema Archive | 1999


    Corrosion data system for marine steel structures

    Yamamoto, M. / Nogami, A. / Hirosawa, N. | Tema Archive | 1989