Coating with suitable grease found to inhibit stress-corrosion cracking in bore of inner race of ball-bearing assembly operating in liquid oxygen. Protects bore and its corner radii from corrosion-initiating and -accelerating substances like moisture and contaminants, which enter during assembly. Operating life extended at low cost, and involves very little extra assembly time.


    Access

    Access via TIB

    Check availability in my library


    Export, share and cite



    Title :

    Grease Inhibits Stress-Corrosion Cracking In Bearing Race


    Contributors:

    Published in:

    Publication date :

    1991-08-01



    Type of media :

    Miscellaneous


    Type of material :

    No indication


    Language :

    English


    Keywords :


    Reducing Stress-Corrosion Cracking in Bearing Alloys

    Paton, N. E. / Dennies, D. P. / Lumsden, I., J.b. | NTRS | 1986


    Controlling stress-corrosion cracking

    Franklin, D. B. / Herring, H. W. / Humphries, T. S. et al. | NTRS | 1977



    On the Stress Corrosion Cracking

    Karlinski, W. / Szachnowski, W. | British Library Online Contents | 1995