Coating with suitable grease found to inhibit stress-corrosion cracking in bore of inner race of ball-bearing assembly operating in liquid oxygen. Protects bore and its corner radii from corrosion-initiating and -accelerating substances like moisture and contaminants, which enter during assembly. Operating life extended at low cost, and involves very little extra assembly time.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Grease Inhibits Stress-Corrosion Cracking In Bearing Race


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    01.08.1991



    Medientyp :

    Sonstige


    Format :

    Keine Angabe


    Sprache :

    Englisch


    Schlagwörter :


    Reducing Stress-Corrosion Cracking in Bearing Alloys

    Paton, N. E. / Dennies, D. P. / Lumsden, I., J.b. | NTRS | 1986


    Controlling stress-corrosion cracking

    Franklin, D. B. / Herring, H. W. / Humphries, T. S. et al. | NTRS | 1977



    On the Stress Corrosion Cracking

    Karlinski, W. / Szachnowski, W. | British Library Online Contents | 1995