Resistance to stress-corrosion cracking in some stainless-steel alloys increased by addition of small amounts of noble metals. 0.75 to 1.00 percent by weight of palladium or platinum added to alloy melt sufficient to improve properties of certain stainless steels so they could be used in manufacture of high-speed bearings.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Reducing Stress-Corrosion Cracking in Bearing Alloys


    Beteiligte:
    Paton, N. E. (Autor:in) / Dennies, D. P. (Autor:in) / Lumsden, I., J.b. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1986-01-01



    Medientyp :

    Sonstige


    Format :

    Keine Angabe


    Sprache :

    Englisch


    Schlagwörter :


    Stress corrosion cracking of titanium alloys.

    Beck, T. R. / Blackburn, M. J. | NTRS | 1968


    Stress corrosion cracking of titanium alloys.

    BECK, T. R. / BLACKBURN, M. J. | AIAA | 1968


    STRESS CORROSION CRACKING OF TITANIUM ALLOYS

    BECK, T. / BLACKBURN, M. | AIAA | 1967


    Stress Corrosion Cracking Tests of Aerospace Alloys

    Dietzel, W. / European Space Agency | British Library Conference Proceedings | 2014


    Stress Corrosion Cracking of Certain Aluminum Alloys

    Hasse, K. R. / Dorward, R. C. | NTRS | 1983