Der Spanwinkel beeinflußt Art und Umfang der Werkstoffbeanspruchung, indem mit kleiner und negativ werdendem Spanwinkel die Stauchwirkung und damit die Scherverformung zunimmt. Daraus ergibt sich der Wechsel vom gleichförmigen Fließspan bei 45° bis zur unregelmäßigen Scherspanbildung bei -20°. Geringe Zeitdehnung.
The film shows the process of chip formation on a polished and etched specimen of C 45 W 3 unalloyed tool steel. The various phenomena of chip formation and the individual deformation processes can be observed particularly well in the perlitic-ferritic structure of the material. The rake angle affects the type and extent of the stresses and strains to which the material is subjected in that the upsetting action and hence the shear strain increase as the positive rake angle becomes smaller and eventually turns negative. From this results the change from uniform flow chips at +45 degrees to irregular shear chips (curl chips) at -20 degrees.
Zerspanen von Stahl C 45 W 3: Schnittvorgang im Feingefüge Variation des Spanwinkels
Documentation/Report
Machining of C 45 W 3 Steel - Cutting Process in the Microstructure; Variation of the Rake Angle
1975-01-01
55MB, 00:04:31:00
Stummfilm
Silent movie
Audio-visual
Audio-visual
Unknown
Aufbauschneidenbildung , Zerspanung / Stahl , Stahl / Zerspanung , Spanbildung / Fließspanbildung / Metall , Spanbildung / Scherspanbildung / Metall , Technik , Fertigungstechnik , spanende Bearbeitung , Stahl machining / steel , steel / machining , chip formation / metal , built-up edge formation , Encyclopaedia Cinematographica , technology , production engineering , swarf machining , steel
Zerspanen metallischer Werkstoffe - Spanentstehung: Schnittvorgang im Feingefüge
TIB AV-Portal | 1977
|Zerspanen von Stahl C 45 W 3: Schnittvorgang im Feingefüge Variation des Schneidenradius
TIB AV-Portal | 1975
|Zerspanen von Stahl 100 Cr 6: Schnittvorgang im Feingefüge
TIB AV-Portal | 1975
|