The results of exposure test in marine environment of Okinawa for 5 years. The concentration of chloride ions in concrete were about 3000-4000 ppm at the 2 cm of surface of concrete with exposed in marine environment and more slowly decreased at deeper position, but they are tended to increases again near the bar. For bare bars of non-cracked concrete specimens after 5 years, cover concrete cracked by the expanding force of red rust, then, maximum depth of pits were as deep as 2.8 mm with concrete covering depth 2 cm in marine atmosphere. For galvanized bar, a maximum depth of pit as deep as 0.9 mm when the concrete covering depth was 2 cm with non-cracked and seawater, maximum depth of pit was deep from 3 mm to 4 mm with cracked. Epoxy coated bar without coating damage did not corrode, irrespective of covering depth, mixing water, cracking concrete and exposed to environment. The corroded pit with coating damage are smaller than bare and galvanized bars.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Corrosion resistance of epoxy coated bar in marine concrete structures


    Weitere Titelangaben:

    Korrosionsbeständigkeit von Bewehrungsstahl mit Epoxyharzüberzug in meerestechnischen Betonkonstruktionen


    Beteiligte:
    Arai, T. (Autor:in) / Ohono, T. (Autor:in) / Shiotani, C. (Autor:in)


    Erscheinungsdatum :

    1989


    Format / Umfang :

    8 Seiten, 5 Bilder, 3 Tabellen, 2 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Epoxy-Coated Rebar for Marine Structures

    Burke, D. F. / ASCE / Committee on Ports and Harbors| Permanent International Association of Navigation Congresses et al. | British Library Conference Proceedings | 1995


    Corrosion of epoxy-coated rebar in marine bridges - Part 1: A 30-year perspective

    Sagues, A.A. / Lau, K. / Powers, R.G. et al. | Tema Archiv | 2010


    Corrosion resistance of aluminium coated stainless steel sheet under marine environment

    Hatanaka, N. / Hattori, Y. / Miyoshi, Y. et al. | Tema Archiv | 1989


    Corrosion protection and repair of marine concrete structures by electrodeposition method

    Kumada, M. / Sasaki, H. / Yokota, M. et al. | Tema Archiv | 1989