The extent of corrosion of epoxy-coated rebar (ECR) in marine bridges was found to be generally correlated with concrete chloride diffusivity, DApp, with significant corrosion observed for bridges with DApp values reaching up to ~10-7 cm2/s but not for sound concrete locations in bridges with DApp approaching the order of 10-9 cm2/s. However, significant ECR corrosion was observed in several preexisting cracked concrete locations of a low DApp bridge after only ~15 years of service. Well manifested, enhanced chloride and moisture penetration took place through the preexisting cracks of this bridge. The corrosion products in that case were solid and grew underneath the epoxy coating and had a composition consistent with that of chloride-substituted Akaganeite (beta-FeO[OH]). Laboratory experiments showed that oxygen presence was not necessary for the formation of similar corrosion products, suggesting that corrosion damage could develop even with thin, moisture-filled cracks that would restrict oxygen flow to the corroding region. Other surveyed low DApp bridges built with ECR showed also preferential chloride penetration at cracks, but no corrosion. An initial model formulation is introduced that may serve as a starting point for quantitative corrosion forecasting of possible damage in those other bridges. Exploratory projections indicate that, as expected, relatively isolated preexisting cracking should only create topical concrete damage with limited maintenance requirements. However, if the preexisting crack orientation with respect to the rebar were adverse and chloride transport were greatly enhanced (as it could be expected in relatively wide cracks), projected corrosion damage was more substantial.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Corrosion of epoxy-coated rebar in marine bridges - Part 2: Corrosion in cracked concrete


    Weitere Titelangaben:

    Korrosion von epoxidharzbeschichtetem Armierungsstahl in Meeresbrücken - Teil 2: Korrosion in gerissenem Beton


    Beteiligte:
    Lau, K. (Autor:in) / Sagues, A.A. (Autor:in) / Powers, R.G. (Autor:in)

    Erschienen in:

    Corrosion, Houston ; 66 , 6 ; 065002/1-065002/16


    Erscheinungsdatum :

    2010


    Format / Umfang :

    16 Seiten, 15 Bilder, 3 Tabellen, 34 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Corrosion of epoxy-coated rebar in marine bridges - Part 1: A 30-year perspective

    Sagues, A.A. / Lau, K. / Powers, R.G. et al. | Tema Archiv | 2010


    Epoxy-Coated Rebar for Marine Structures

    Burke, D. F. / ASCE / Committee on Ports and Harbors| Permanent International Association of Navigation Congresses et al. | British Library Conference Proceedings | 1995


    Corrosion resistance of epoxy coated bar in marine concrete structures

    Arai, T. / Ohono, T. / Shiotani, C. | Tema Archiv | 1989



    How to Halt Corrosion on Concrete Bridges

    British Library Online Contents | 1994