a-C:H (hydrogenated amorphous carbon) films were prepared on silicon and steel substrates by medium frequency unbalanced magnetron sputtering with Ar (argon) and CH4 (methane) as the source gases. The effect of annealing temperature in vacuum on the microstructure as well as mechanical properties and tribological behaviour of as-prepared a-C:H films were investigated. The friction and wear behaviours of the films in different environments (vacuum, N2, and air) were evaluated with a pin-on-disk tribometer; and their sliding lifetime in vacuum was discussed in relation to friction and wear mechanisms. Results show that annealing in vacuum at a low temperature of up to 200 °C causes little change in the microstructure and hardness of a-C:H films but reduces their internal stress and surface roughness to some extent. These annealed films exhibit excellent antiwear ability in all test environments and show promising potential as a kind of space lubricants. The film begins to release hydrogen and increases the content of graphite-like structure at about 300 °C. As a result, a-C:H films annealed above 200 °C have increased surface roughness as well as reduced hardness, internal stress, and wear resistance in all test environments.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of vacuum annealing on the microstructure and triboiogical behavior of hydrogenated amorphous carbon films prepared by magnetron sputtering


    Beteiligte:
    Wu, Yanxia (Autor:in) / Li, Hongxuan (Autor:in) / Ji, Li (Autor:in) / Liu, Liu (Autor:in) / Ye, Yinping (Autor:in) / Chen, Jianmin (Autor:in) / Zhou, Huidi (Autor:in)


    Erscheinungsdatum :

    2013


    Format / Umfang :

    9 Seiten, 8 Bilder, 46 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Rapid Annealing Of Amorphous Hydrogenated Carbon

    Alterovitz, Samuel A. / Pouch, John J. / Warner, Joseph D. | NTRS | 1989


    A new low-emissivity films Prepared by Magnetron Sputtering

    Shu-rong, Dong / De-miao, Wang | IEEE | 2006


    Characteristics of tantalum oxynitride films prepared by rf magnetron sputtering [4099-30]

    Jong, C. A. / Chin, T. S. / SPIE | British Library Conference Proceedings | 2000



    X-ray reflectometry applied to amorphous carbon thin films prepared by sputtering radio frequency

    Aboudihab, I. / Ech-chamikh, E. / Lessard, R. A. et al. | British Library Conference Proceedings | 2003