Critical fluid velocities and erosion corrosion rates are often limiting production rates in oil and gas production. A combined flow loop - jet impingement pilot plant has been used to determine mass loss rates in mixed gas - saltwater - sand multiphase flow conditions at impact velocities up to 60 m/s. Artificial brine with a salt content of 27 g/l was used as liquid phase. The sand content, with grain size below 150 my m, was up to five times higher than field conditions to accelerate testing. CO2 at a pressure of 1, 500 kPa was used as the gas phase. Rectangular stainless steel samples were cut out from bars and pipes, mechanically ground and polished prior to testing. Damaged surfaces of specimens exposed to the high velocity multiphase flow were investigated by stereo microscopy, scanning electron microscopy(SEM) and an optical device for 3D surface measurements. Metallographic cross sections of the tested samples were prepared to characterize the microstructure underneath the damaged surface areas. Electrochemical investigations according to ASTM G 61 were performed to determine electrochemical behavior of tested materials including critical pitting potentials Epit and repassivation potentials Erepass.
How do microstructure and pren affect the erosion corrosion behaviour of stainless steels?
2009
13 Seiten, 31 Quellen
Aufsatz (Konferenz)
Englisch
dreidimensionale Darstellung , Erdölfernleitung , Erosionskorrosion , flüssige Phase , Gasfernleitung , Korrosionsgeschwindigkeit , Korrosionsprüfung , korrosiver Verschleiß , kritische Geschwindigkeit , Lochfraßkorrosion , Lochkorrosionspotenzial , Mehrphasenströmung , Mischgas , nichtrostender Stahl , Oberflächenschaden , Partikelströmung , Pilotanlage , Rasterelektronenmikroskopie , Rohrstahl , Stereomikroskopie , Strömungsgeschwindigkeit
Streustrombewertungen gemäß prEN 50122-2
Tema Archiv | 2008
|Streustrombewertungen gemäß prEN 50122-2
IuD Bahn | 2008
|Energieversorgung - Streustrombewertungen gemäss prEN 50122-2
Online Contents | 2008
|Marine Biofilms on Stainless Steels: Effects on the Corrosion Behaviour
British Library Conference Proceedings | 1998
|Investigation of pitting corrosion behaviour of welded duplex stainless steels
Kraftfahrwesen | 1994
|