The work presents the electrochemical results obtained during the study of the corrosion of X52 pipeline steel sample, immersed in brines containing H2S, under turbulent flow conditions. Linear polarisation resistance (LPR), electrochemical impedance spectroscopy (EIS), Electrochemical Noise (EN) and polarisation curves were used in order to determine the effect of turbulent flow upon the corrosion kinetics of the steel. It was found that flow has a considerable influence upon the electrochemical process occurring on the surface of the steel and the corrosion rate is increased.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effects of turbulent flow on the corrosion kinetics of X52 pipeline steel in aqueous solutions containing H2S


    Beteiligte:

    Erschienen in:

    Materials and Corrosion ; 55 , 8 ; 586-593


    Erscheinungsdatum :

    2004


    Format / Umfang :

    8 Seiten, 15 Bilder, 2 Tabellen, 29 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Corrosion kinetics of pipeline carbon steel weld immersed in aqueous solution containing H2S

    Avendano-Castro, C. / Galvan-Martinez, R. / Contreras, A. et al. | Tema Archiv | 2009


    Turbulent flow device in pipeline

    YANG JUNDONG / LUO DONGHAO / LIANG ZHANXIN | Europäisches Patentamt | 2020

    Freier Zugriff


    Pitting corrosion in pipeline steel weld zones

    Chaves, Igor A. / Melchers, Robert E. | Tema Archiv | 2011