The aim of this research was to investigate the cause of the severe localised corrosion that sometimes occurs at welds in carbon steel pipelines carrying hydrocarbons and inhibited brines saturated with carbon dioxide. A rotating cylinder electrode apparatus was designed so that electrodes machined from the weld metal, heat affected zone and parent material of welded X65 pipeline steel could be galvanically coupled and tested in high shear stress conditions. The galvanic currents flowing between the weld regions were recorded using zero resistance ammeters, and their self-corrosion rates were found by polarisation resistance measurements. The total corrosion rate of each weld region was obtained from the sum of the self-corrosion and galvanic contributions. In uninhibited conditions, the weld metal and heat affected zone were both cathodic to the parent material, and localised corrosion was prevented. However, when an oilfield corrosion inhibitor was present, a current reversal took place, which resulted in accelerated weld corrosion. The inhibitor consisted of a blend of neutralising amines and synergists in a water/glycol based solvent package. Electrochemical impedance spectroscopy showed that the inhibitor film had lower electrical resistance and was less protective on the weld metal than on the parent material. At the highest shear stress, a second current reversal could occur when the inhibitor was removed from all regions of the weld, and there was a return to the original galvanic behaviour. It was concluded that preferential weld corrosion was caused by unstable conditions in which the inhibitor film was selectively disrupted on the weld metal but remained effective on the other weld regions.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Preferential weld corrosion of X65 pipeline steel in flowing brines containing carbon dioxide


    Weitere Titelangaben:

    Bevorzugte Schweißnahtkorrosion von Rohrstahl X65 in fließender CO2-haltiger Salzlösung


    Beteiligte:
    Alawadhi, K. (Autor:in) / Robinson, M.J. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2011


    Format / Umfang :

    12 Seiten, 18 Bilder, 1 Tabelle, 21 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Inhibition of weld corrosion in flowing brines containing carbon dioxide

    Alawadhi, K. / Robinson, M. / Chalmers, A. et al. | Tema Archiv | 2008


    Corrosion of C-Mn-steel and 0.5 % Cr steel in flowing CO2 saturated brines

    Rogne, T. / Eggen, T.G. / Steinsmo, U. | Tema Archiv | 1996


    Corrosion kinetics of pipeline carbon steel weld immersed in aqueous solution containing H2S

    Avendano-Castro, C. / Galvan-Martinez, R. / Contreras, A. et al. | Tema Archiv | 2009


    Pitting corrosion in pipeline steel weld zones

    Chaves, Igor A. / Melchers, Robert E. | Tema Archiv | 2011