The newly developed sheet steel lightly coated with an organic composite is as follows. Zn-Ni alloy plated sheet steel with a coating weight of 30 g/m2 and average Ni concentration of 11.5 ∼12.0 % is chromated through electrolysis. The coating weight of chromate film is 50 ∼90 mg/m2 in Cr. Furthermore, emulsified olefin-acrylic acid copolymer resin mixed with colloidal silica of particle size 7 ∼8 nm applied to a thickness of 1.0 ∼1.8 μm. Olefin-acrylic acid copolymer resin and colloidal silica are mixed at the rate of 100 and 30 (parts by weight). It maintains excellent corrosion resistance even after forming, C-ED paint corrosion resistance and paint adhesion. Furthermore, it has excellent perforation resistance. The product has excellent weldability and is well suited to continuous forming, too. These excellent properties of the newly developed sheet steel lightly coated with an organic composite are obtained by emulsified olefin-acrylic acid copolymer resin and mixed colloidal silica.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Properties of a Newly Developed Organic Composite Coated Steel Sheet for Automotive Use


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Odashima, Hisao (Autor:in) / Kikuchi, Ikuo (Autor:in) / Shibata, Keitaro (Autor:in)

    Kongress:

    International Congress & Exposition ; 1992



    Erscheinungsdatum :

    01.02.1992




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Properties of a newly developed organic composite coated steel sheet for automotive use

    Odashima,H. / Shibata,K. / Kikuchi,I. et al. | Kraftfahrwesen | 1992


    Properties of a newly developed organic composite coated steel sheet for automotive use

    Odashima, H. / Shibata, K. / Kikuchi, I. | Tema Archiv | 1992


    Newly Developed Organic Composite-Coated Steel Sheet with Bake-Hardenability

    Kurosawa, Mitsumasa / Kobayashi, Shigeru / Tsugawa, Shun-ichi et al. | SAE Technical Papers | 1986


    Newly Developed Organic Composite-Coated Steel Sheet with Bake-Hardenability

    Mohri,T. / Tsugawa,S. / Kobayashi,S. et al. | Kraftfahrwesen | 1986


    Newly developed organic-silicate composite coated steel sheet with bake hardenability

    Yamashita, M. / Kubota, T. / Watanabe, T. et al. | Tema Archiv | 1989