To improve the performance of zinc-rich painted steel sheets, such as Zincrometal®, we at first developed Zn-Ni plated steel sheet with a thin (about 1μm) organic-silicate composite film entirely different from a zinc-rich paint film. This product (EZN-UC) is superior to zinc-rich painted steel sheet in corrosion resistance, anti-powdering property and weldability. This product (EZN-UC), however, is not able to provide bake hardenability due to the high curing temperature of the film. In response to increasing demand for the product with bake hardenability, we have developed new organic-silicate composite coated steel sheet (EZN-UCII), which allows the coating to be cured in the temperature range, where bake hardenability can be maintained. The new product (EZN-UCII) attained higher corrosion resistance than the usual product (EZN-UC) by adopting a new organic-silicate composite, and also provides excellent weldability, anti-powdering property and paint-ability equivalent to the usual product (EZN-UC).


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Newly Developed Organic-Silicate Composite Coated Steel Sheet with Bake Hardenability


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1989



    Erscheinungsdatum :

    1989-02-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Newly developed organic-silicate composite coated steel sheet with bake hardenability

    Yamashita, M. / Kubota, T. / Watanabe, T. et al. | Tema Archiv | 1989


    Newly developed organic-silicate composite coated steel sheet with bake hardenability

    Yamashita,M. / Kubota,T. / Watanabe,T. et al. | Kraftfahrwesen | 1989


    Newly Developed Organic Composite-Coated Steel Sheet with Bake-Hardenability

    Mohri,T. / Tsugawa,S. / Kobayashi,S. et al. | Kraftfahrwesen | 1986


    Newly Developed Organic Composite-Coated Steel Sheet with Bake-Hardenability

    Kurosawa, Mitsumasa / Kobayashi, Shigeru / Tsugawa, Shun-ichi et al. | SAE Technical Papers | 1986


    Newly-developed organic composite-coated steel sheet with high perforation resistance

    Shun-ichi,T. / Mohri,T. / Kobayashi,S. et al. | Kraftfahrwesen | 1985