A new organic composite-coated steel sheet with bake-hardenability has been developed. The steel sheet consists of Zn-Ni alloy electroplated layer, chromate and zinc powder free organic film. To obtain better formability (anti-powdering) and weldability, the thickness of the organic film is reduced to 0.8∼1.5µm (1.0∼2.0g/m2). The addition of bake-hardenability to this organic coated steel sheet was realized by controlling the amount of residual solute carbon in continuous annealed extra low carbon steels.Corrosion resistance, formability and weldability of the obtained steel sheet were investigated.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Newly Developed Organic Composite-Coated Steel Sheet with Bake-Hardenability


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    1986 SAE Automotive Corrosion and Prevention Conference and Exposition ; 1986



    Erscheinungsdatum :

    1986-12-08




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Newly Developed Organic Composite-Coated Steel Sheet with Bake-Hardenability

    Mohri,T. / Tsugawa,S. / Kobayashi,S. et al. | Kraftfahrwesen | 1986


    Newly developed organic-silicate composite coated steel sheet with bake hardenability

    Yamashita, M. / Kubota, T. / Watanabe, T. et al. | Tema Archiv | 1989


    Newly developed organic-silicate composite coated steel sheet with bake hardenability

    Yamashita,M. / Kubota,T. / Watanabe,T. et al. | Kraftfahrwesen | 1989


    Newly Developed Organic-Silicate Composite Coated Steel Sheet with Bake Hardenability

    Kabasawa, Makoto / Yamashita, Masaaki / Nishimoto, Tadashi et al. | SAE Technical Papers | 1989


    Newly-developed organic composite-coated steel sheet with high perforation resistance

    Shun-ichi,T. / Mohri,T. / Kobayashi,S. et al. | Kraftfahrwesen | 1985