A new type of bake-hardenable high strength hot-rolled sheet steel was developed, which shows a remarkable increase in tensile strength as well as yield strength after strain age hardening without addition of special elements. Then the impact absorption energy of the developed steel was evaluated by the finite element method using a hat square column model. The equivalent thickness and tensile strength of the developed steel assuming use as a substitute for the conventional 440MPa steel were clarified.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    FEM Analysis of Crashworthiness of Hot-Rolled Sheet Steel with Excellent Bake Hardenability in Tensile Strength


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Abe, H. (Autor:in) / Hiramoto, J. (Autor:in) / Kaneko, S. (Autor:in) / Hira, T. (Autor:in)

    Kongress:

    International Body Engineering Conference & Exposition ; 2003



    Erscheinungsdatum :

    27.10.2003




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    20037085 2003-01-2808 FEM Analysis of Crashworthiness of Hot-Rolled Sheet Steel with Excellent Bake Hardenability in Tensile Strength

    Hiramoto, J. / Kaneko, S. / Hira, T. et al. | British Library Conference Proceedings | 2003


    Newly Developed Organic Composite-Coated Steel Sheet with Bake-Hardenability

    Mohri,T. / Tsugawa,S. / Kobayashi,S. et al. | Kraftfahrwesen | 1986


    Newly Developed Organic Composite-Coated Steel Sheet with Bake-Hardenability

    Kurosawa, Mitsumasa / Kobayashi, Shigeru / Tsugawa, Shun-ichi et al. | SAE Technical Papers | 1986


    Newly Developed Organic-Silicate Composite Coated Steel Sheet with Bake Hardenability

    Kabasawa, Makoto / Yamashita, Masaaki / Nishimoto, Tadashi et al. | SAE Technical Papers | 1989


    Newly developed organic-silicate composite coated steel sheet with bake hardenability

    Yamashita, M. / Kubota, T. / Watanabe, T. et al. | Tema Archiv | 1989