1.55 /spl mu/m wavelength GaInAsP-InP quantum-wire lasers fabricated by two-step OMVPE growth and EBX lithography are characterized and compared with single-quantum-film lasers prepared on the same wafer. A clear anisotropic PL property as well as a blue shift energy corresponding to the wire width was confirmed. Higher differential quantum efficiency with lower threshold current operation (I/sub th/=5.5 mA, J/sub th/=34A/cm/sup 2/ at 90 K) was obtained at temperature region T<170 K.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fabrication and characterization of GaInAsP/InP long wavelength quantum-wire lasers


    Beteiligte:
    Arai, S. (Autor:in)


    Erscheinungsdatum :

    01.01.1997


    Format / Umfang :

    245808 byte





    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    Fabrication and Characterization of GaInASP/InP Long Wavelength Quantum-Wire Lasers

    IEEE; Lasers and Electro-Optics Society | British Library Conference Proceedings | 1997


    Temperature Sensitivity of Oscillation Wavelength in 1.3m- GaInAsP/InP Quantum-Well Semiconductor Lasers

    IEEE; Lasers and Electro-Optics Society | British Library Conference Proceedings | 1996


    Mass-Transported GaInAsP/InP Lasers

    Z. L. Liau / J. N. Walpole | NTIS | 1989