The fatigue life of GH4169 superalloy plate with central hole was tested at 663 MPa/20 ℃ before and after cold expansion(CE). The fatigue fractures, the evolution of residual stress fields and surface morphology were respectively analyzed by scanning electron microscope, X-ray diffraction residual stress tester and surface profilometer. The results show that CE increases the fatigue life with the hole structure to 2.6 times compared with as-received. As the result of hole wall surface strengthening by CE, the fatigue source of CE specimens is single originated from chamfering, while the original ones are multi-source and sprouted at the hole wall. The CE surface residual stresses relax during 50000 cycles fatigue process, and however, about 55% and 75% compressive residual stresses are still retained at the inlet and outlet ends respectively. Moreover, CE reduces the surface roughness of the hole wall from Ra 0.354 μm to Ra 0.297 μm.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effect of cold expansion on room-temperature low cycle fatigue life of GH4169 superalloy with hole structure


    Beteiligte:
    XU Chunling (Autor:in) / WANG Xin (Autor:in) / SONG Yinggang (Autor:in) / WANG Qiang (Autor:in) / LUO Xuekun (Autor:in) / TANG Zhihui (Autor:in)


    Erscheinungsdatum :

    2020




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Effect of Surface Integrity of Turned GH4169 Superalloy on Fatigue Performance

    WU Daoxia / ZHANG Dinghua / YAO Changfeng | DOAJ | 2017

    Freier Zugriff


    Experimental on ultrahigh frequency vibration fatigue of GH4169 nickel-based superalloy

    WANG Zhaohan / PAN Kai / CHEN Yonghui et al. | DOAJ | 2025

    Freier Zugriff

    Effect of Cold Expansion on Fatigue Life of Hole Structure of TC17 Titanium Alloy

    AI Yingjun / WANG Xin / SONG Yinggang et al. | DOAJ | 2017

    Freier Zugriff

    Surface oxidation characteristics of nickel-base superalloy GH4169 powder

    Zhang Lichong / Xu Wenyong / Li Zhou et al. | DOAJ | 2020

    Freier Zugriff