Through turning and rotary bending fatigue test, the effect of turning feed on GH4169 superalloy surface integrity, and the effect of surface integrity on fatigue life were studied. The results show that the surface roughness Ra decreases from 1.497 μm to 0.431 μm when the turning feed decreases from 0.2 mm/r to 0.02 mm/r. The surface residual stresses are changed from tensile stress to compressive stress. The depth of plastic deformation layer decreases from 8 μm to 2 μm. The surface stress concentration factor has the most significant effect on the fatigue life of GH4169. With the increase of stress concentration factor, the fatigue life decreases significantly. When f is 0.13 mm/r, the surface stress concentration factor Kst is 1.166; the surface micro-hardness is 405.27HV0.025; the surface residual stress is 82.08MPa; and the average fatigue life is 6.98×104 cycles. The multiple cracks are initiated at the machined surface defects of GH4169 superalloy specimen.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effect of Surface Integrity of Turned GH4169 Superalloy on Fatigue Performance


    Beteiligte:
    WU Daoxia (Autor:in) / ZHANG Dinghua (Autor:in) / YAO Changfeng (Autor:in)


    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Experimental on ultrahigh frequency vibration fatigue of GH4169 nickel-based superalloy

    WANG Zhaohan / PAN Kai / CHEN Yonghui et al. | DOAJ | 2025

    Freier Zugriff

    Surface oxidation characteristics of nickel-base superalloy GH4169 powder

    Zhang Lichong / Xu Wenyong / Li Zhou et al. | DOAJ | 2020

    Freier Zugriff



    Effect of cold expansion on room-temperature low cycle fatigue life of GH4169 superalloy with hole structure

    XU Chunling / WANG Xin / SONG Yinggang et al. | DOAJ | 2020

    Freier Zugriff