In order to improve the fatigue performance of TC17 central hole specimen, the hole wall surface integrity was characterized by scanning electron microscopy (SEM), roughness meter, X-ray diffraction, and the influence of hole cold expansion(HCE) parameter on the fatigue performance of the hole specimens was investigated. The results show that the minimum fatigue life (14718 cycle) of the HCE specimens with an expansion value of 0.18 mm is higher than the original specimen (13965 cycle). Compared to the specimens with the expansion values of 0.28 mm and 0.38 mm, the fatigue life dispersion is less, no obvious stress concentration phenomenon is found, and it has the best fatigue performance than the other two. The surface roughness value of hole wall is the lowest after the HCE with 0.18 mm, the inner hole wall forms a certain depth of strengthened layer, the residual compressive stress produced in the hole side effectively suppresses the produce of fatigue cracks in the inner hole wall, so the fatigue performance of hole structure is improved.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effect of Cold Expansion on Fatigue Life of Hole Structure of TC17 Titanium Alloy


    Beteiligte:
    AI Yingjun (Autor:in) / WANG Xin (Autor:in) / SONG Yinggang (Autor:in) / WANG Qiang (Autor:in) / LUO Xuekun (Autor:in) / TANG Zhihui (Autor:in) / ZHAO Zhenye (Autor:in)


    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt





    Effect of Double Cold Expansion of Hole on Fatigue Property of TB6 Titanium Alloy

    LUO Xuekun / AI Yingjun / WANG Xin et al. | DOAJ | 2017

    Freier Zugriff

    Cold Expansion Strengthening of 7050 Aluminum Alloy Hole: Structure, Residual Stress, and Fatigue Life

    Qi Li / Qichao Xue / Quansheng Hu et al. | DOAJ | 2022

    Freier Zugriff

    Effect of High-Speed Milling Parameters on Surface Metamorphic Layer of TC17 Titanium Alloy

    TAN Liang / ZHANG Dinghua / YAO Changfeng | DOAJ | 2017

    Freier Zugriff

    Numerical Simulation of TC17 Titanium Alloy Thin Blade Strengthened by Laser Shock Processing

    Ma, Sijie / Ding, Xiangyu / Yang, Zhi et al. | Springer Verlag | 2022