GH3536 superalloy was fabricated using Selective Laser Melting (SLM) to investigate the effect of process parameters including the laser power and scanning speed on the density, microscopic defects and surface quality of GH3536 samples. According to the measurement of density, it can be found that the density of samples increases rapidly when the laser energy density is less than 57.0 J/mm3, the density of samples fluctuates within the range of 8.30 g/cm3-8.35 g/cm3 as the laser energy density increases from 57.0 J/mm3 to 187.0 J/mm3, while the density of samples decreases slightly when the laser energy further increases. The conclusion is that the inadequate or excessive energy input reduces the density of samples. The metallographic observation shows that there are a large number of lack-of-fusion defects when the laser energy is insufficient. However, when the input laser energy is too much, many evenly distributed microcracks and gas pores appear inside of samples, indicating that defects are the main reason for low density of samples. The optimal process parameters of SLM-processed GH3536 alloy are determined by the statistical analysis of spatter particles which might cause irregular defects. Tensile properties of the sample fabricated under 175 W and 700 mm/s are tested at room temperature and the results show that the SLM-ed GH3536 superalloy has good tensile properties at room temperature.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effect of SLM process parameters on microscopic defects and surface quality of GH3536 superalloy


    Beteiligte:
    ZHANG Xuan (Autor:in) / DONG Anping (Autor:in) / DU Dafan (Autor:in) / PAN Yunwei (Autor:in) / XIONG Lianghua (Autor:in) / KONG Yuan (Autor:in) / SUN Baode (Autor:in)


    Erscheinungsdatum :

    2022




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Effect of heat treatment on high temperature tensile properties of selective laser melting GH3536 alloys

    HUANG Shuai / QU Zhiqi / ZHANG Guohui et al. | DOAJ | 2024

    Freier Zugriff


    Effect of Parameters of HRS Process on Microstructure of DZ466 Ni-based Superalloy

    JIANG Hua / BAO Yunfei / LI Qing et al. | DOAJ | 2018

    Freier Zugriff

    The Effect of Superalloy Structure on Ultrasonic Wave Parameters

    Nawrocki Jacek / Gancarczyk Kamil / Manaj Wojciech et al. | DOAJ | 2015

    Freier Zugriff

    Effect of Surface Integrity of Turned GH4169 Superalloy on Fatigue Performance

    WU Daoxia / ZHANG Dinghua / YAO Changfeng | DOAJ | 2017

    Freier Zugriff