The influences of withdrawal rate and mold heater zone temperature during high rate solidification (HRS) on the microstructures were investigated. As the results, the primary dendritic spacing, the size of γ′ phase particles and carbides are decreased with the increase of the withdrawal rate or mold heater zone temperature. As the withdrawing goes on, the primary dendritic spacing and the size of γ′ phase particles are increased, and the heat emission efficiency of HRS process is decreased. The results show that fine dendrite and γ′ phase can be achieved with the withdrawal of 8 mm/min and mold heater zone temperature of 1520 ℃/1530 ℃, which is benefit to improve the properties of DZ466 alloy.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effect of Parameters of HRS Process on Microstructure of DZ466 Ni-based Superalloy


    Beteiligte:
    JIANG Hua (Autor:in) / BAO Yunfei (Autor:in) / LI Qing (Autor:in) / YANG Zhenyu (Autor:in) / CHEN Jingyang (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    The Effect of Superalloy Structure on Ultrasonic Wave Parameters

    Nawrocki Jacek / Gancarczyk Kamil / Manaj Wojciech et al. | DOAJ | 2015

    Freier Zugriff

    Effect of SLM process parameters on microscopic defects and surface quality of GH3536 superalloy

    ZHANG Xuan / DONG Anping / DU Dafan et al. | DOAJ | 2022

    Freier Zugriff


    Effect of C Content on Microstructure of Second Generation Single Crystal Superalloy

    LIU Shizhong / SHI Zhenxue / LI Jiarong | DOAJ | 2017

    Freier Zugriff