The cracking resistance of asphalt concrete (AC) that contains reclaimed asphalt pavement (RAP) was evaluated in this study with a fracture energy approach. Monotonic and cyclic semicircular bending (SCB) tests were performed with the digital image correlation to correlate crack length with fracture energy. Five types of AC that contained various RAP content (0%, 15%, 30%, 40%, 50%) were evaluated at two intermediate temperatures (15°C and 25°C). On the basis of the relationship between fracture energy and crack extension length, several performance indicators for cracking were proposed: fracture energy and crack initiation energy in monotonic and cyclic SCB tests, an energy cumulative rate in monotonic SCB tests, a fatigue accumulation index (FAI), a fracture energy index, and the slope of the crack steady propagation stage (SOCSP) in cyclic SCB tests. The effects of the RAP content on these indicators were investigated. It was observed from the test results that RAP reduced the fracture energy and crack initiation energy in the monotonic and the cyclic SCB tests. RAP led to a lower energy cumulative rate than an AC mix without RAP in the monotonic SCB tests. Similarly, the FAI and SOCSP values were found to decrease with an increase in RAP content in the cyclic SCB tests. These results indicated that, in general, the addition of RAP reduced the cracking resistance at intermediate temperatures.


    Access

    Download

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Cracking Resistance Characterization of Asphalt Concrete Containing Reclaimed Asphalt Pavement at Intermediate Temperatures


    Additional title:

    Transportation Research Record


    Contributors:
    Zhou, Zhou (author) / Gu, Xingyu (author) / Ni, Fujian (author) / Li, Qiang (author) / Ma, Xiang (author)


    Publication date :

    2017-01-01




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    English



    Field Aging and Binder Fatigue Performance of Intermediate Asphalt Concrete Layers Containing Reclaimed Asphalt Pavement

    Rahman, Mohammad A. / Harvey, John T. / Jiao, Liya et al. | Transportation Research Record | 2024

    Free access

    Cracking performance characterisation of asphalt mixtures containing reclaimed asphalt pavement with hybrid binder

    Yan, Yu / Roque, Reynaldo / Hernando, David et al. | British Library Online Contents | 2019


    Variability Analysis of Hot-Mix Asphalt Concrete Containing High Percentage of Reclaimed Asphalt Pavement

    Solaimanian, Mansour / Tahmoressi, Maghsoud | Transportation Research Record | 1996



    Asphalt Pavements with High Reclaimed Asphalt Pavement Content

    Aurangzeb, Qazi / Al-Qadi, Imad L. | Transportation Research Record | 2014