Teflon fluorinated ethylene propylene (FEP) is used on the Hubble Space Telescope (HST) as the outer layer of multilayer insulation (MLI) blankets. During space shuttle servicing missions (SM) to HST through thickness cracks were observed in the FEP layers. Material brought to Earth for investigation showed signs of severe degradation. During servicing mission 3B, the 4th servicing mission to HST in March 2002, the second pair of European Space Agency ESA built solar arrays was retrieved and flown back to Earth after 8.25 years in space. Samples of the MLI thermal control material were taken from the solar array drive arm (SADA) and investigated for surface and bulk degradation. The MLI was enveloped around the SADA and thus allowed the examination of FEP degradation in dependence of the orientation of space exposed areas with respect to the sun. Therefore micrographs of FEP surfaces and fractographs of through thickness cracks were taken and the solar absorptance alpha s and the normal emittance epsilon N was measured on the entire MLI. Differential scanning calorimetrical analyses as well as electron spectroscopy for chemical analyses were conducted to analyze chemical changes of the bulk polymer and the surface layer, respectively. Tensile properties and mass losses of the space exposed material were evaluated as well. Results of the investigated thermal control material are compared with samples exposed on the ground to thermal cycling, soft X-rays and vacuum ultra-violet radiation as well as to previously reported results on space-exposed FEP. The paper thus gives further insight into the mechanism and processes contributing to the on orbit degradation of Teflon FEP and correlates the presented data with exposure levels and exposure conditions.


    Access

    Access via TIB

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Surface and bulk degradation of Teflon FEP retrieved from the Hubble Space Telescope solar arrays


    Additional title:

    Der Abbau der Oberfläche und der Formmasse des aus den Solarzellen des Hubble-Weltraumteleskops zurückgewonnenen Teflons FEP


    Contributors:


    Publication date :

    2008


    Size :

    18 Seiten, 7 Bilder, 4 Tabellen, 24 Quellen




    Type of media :

    Conference paper


    Type of material :

    Print


    Language :

    English




    Mechanical properties of teflon FEP retrieved from the Hubble space telescope

    Dever, J.A. / Groh, K.K. de / Messer, R.K. et al. | Tema Archive | 2001


    Analyses of Hubble Space Telescope Aluminized-Teflon Insulation Retrieved After 19 Years of Space Exposure

    Groh, Kim K. / Waters, Deborah L. / Mohammed, Jelila S. et al. | Springer Verlag | 2012


    Mechanical properties degradation of Teflon FEP returned from the Hubble Space Telescope

    Dever, Joyce / de Groh, Kim / Townsend, Jacqueline et al. | AIAA | 1998


    Degradation of Hubble Space Telescope metallized Teflon FEP thermal control materials

    Hansen, P.A. / Townsend, J.A. / Yoshikawa, Y. et al. | Tema Archive | 1998


    Degradation of Hubble Space Telescope aluminized-Teflon bi-stem thermal shields

    Groh, Kim K. de / Snyder, Aaron / Finlay, Katherine A. | Tema Archive | 2008