The corrosion of three-coated electrogalvanized steel (EG) and cold-rolled steel sheet (CR) has been investigated to evaluate their potential for outer side panels of automobile. It was found that, in the salt test, the average width of blisters on the three-coated EG was larger than that on CR. However, in the cyclic corrosion test, which is considered to simulate the actual dry and wet corrosion environment more accurately, CR showed less corrosion resistance, while EG showed high corrosion resistance, that is, no blisters or rust were found on the three-coated EG.


    Access

    Access via TIB

    Check availability in my library


    Export, share and cite



    Title :

    Effect of zinc coating on cosmetic corrosion in automotive body panel


    Additional title:

    Einfluss der Verzinkung auf die kosmetische Corrosion bei Karosserieblechen


    Contributors:
    Honjo, T. (author) / Kurokawa, S. (author) / Kimura, H. (author) / Irie, T. (author)


    Publication date :

    1983


    Size :

    12 Seiten, 12 Bilder, 6 Tabellen, 7 Quellen


    Type of media :

    Conference paper


    Type of material :

    Print


    Language :

    English




    Effect of Zinc Coating on Cosmetic Corrosion in Automotive Body Panel

    Honjo,T. / Kurokawa,S. / Kimura,H. et al. | Automotive engineering | 1983


    Automotive Body Panel Surface Classification

    Wagimin, D. H. / Blount, G. N. / Jones, R. M. et al. | British Library Conference Proceedings | 1998


    Automotive Body Panel Feature Classification

    Harmanto Wagimin, D. / Blount, G. N. / Jones, R. M. | British Library Conference Proceedings | 1998


    Effect of panel surface roughness on automotive coating appearance

    Akutsu,E. / Kurabayashi,O. / Shibano,M. et al. | Automotive engineering | 1985


    Automotive body panel surface classification

    Wagimin,D.H. / Blount,G.N. / Jones,R.M. et al. | Automotive engineering | 1998