Marine aluminum alloy 5456-H343 is a candidate primary structural material for naval high performance ships. This material in the form of 1/8 inch sheet was used to obtain initial alternating surface stress v cycles to failure data in air and salt water. Room temperature tests were performed using deflection controlled fully reversed bending at 30 Hz. Data was obtained for smooth and shallow, sharply notched specimens for fatigue lives up to 10 million cycles. Notches were semi-elliptical surface cracks with depths equal to .002 in., .0115 in., and .025 in. 5456-H343 showed excellent corrosion fatigue resistance in salt water, with increasing environmental sensitivity in the range of 1-10 million cycles. The material exhibits some notch sensitivity at a fatigue life of 10 million cycles. The following fatigue design/failure criterion were developed: (1) for shallow cracks less than .001 in. deep, the maximum fatigue stress is determined by endurance limit or fatigue strength of smooth specimens, and (2) for shallow cracks greater than .020 in. deep, the maximum fatigue stress is determined by the threshold or allowable stress intensity factor of notched specimens. (Kursetz)


    Access

    Access via TIB

    Check availability in my library


    Export, share and cite



    Title :

    Corrosion fatigue of a marine aluminium alloy (5456-H343) in the presence of shallow cracks


    Additional title:

    Korrosionsermuedung der Schiffbau-Aluminiumlegierung (5456-H343) beim Auftreten von flachen Rissen


    Contributors:

    Published in:

    Publication date :

    1978


    Size :

    147 Seiten


    Type of media :

    Report


    Type of material :

    Print


    Language :

    English




    Cathodic kinetics during corrosion of 5456-H 117 aluminium alloy by high velocity sea water

    Watts, A.A. / Davis, J.A. / Gehring, G.A. jun. | Tema Archive | 1977


    Aluminum Alloy 5456, Plate and Sheet

    SAE Technical Papers | 2006


    Aluminum Alloy 5456, Plate and Sheet

    SAE Technical Papers | 1997


    Aluminum Alloy 5456, Plate and Sheet

    SAE Technical Papers | 2012