Abstract Split-sleeve cold expansion processing was employed on the 2024-T3 aluminum alloy plate. Fatigue lives were compared according different expansion, and then the relationship of fatigue life and expansion was analyzed. Residual stresses were measured with different expansion, and the fatigue fractograph was analyzed by SEM. The results show that the split-sleeve cold expansion can obtain longer life compared with the non strengthened hole. The maximum fatigue life increased to 12 times with 6% expansion. When over 6% expansion, fatigue life began to decrease. The split-sleeve cold expansion can form beneficial residual compressive stress, and deferred the fatigue crack initiation. The fatigue fractograph shows quasi-cleavage fracture.
Effect of Strengthened Hole on the Fatigue Life of 2024-T3 Aluminum Alloy
2019-07-03
6 pages
Article/Chapter (Book)
Electronic Resource
English
Influence of hole cold expansion on fatigue resistance of 2024 aluminum alloy
DOAJ | 2020
|Effect of Strengthened Hole on the Fatigue Life of 7050-T7451 Double-Shear Joints
SAE Technical Papers | 2013
|Effect of Strengthened Hole on the Fatigue Life of 7050-T7451 Double-Shear Joints
British Library Conference Proceedings | 2013
|The Effects of Load Sequencing on the Fatigue Life of 2024-T3 Aluminum Alloy
British Library Conference Proceedings | 1996
|