To study the corrosion cracking process of reinforced concrete under the combined effects of chloride and fatigue loading, the constan-current and dry-wet cycle accelerated corrosion method was used to corrosion the specimens under different stress levels for different time. The quality loss of reinforcement, the composition of corrosion products and the cracking of concrete are analyzed from the macro, micro and micro scales, and to obtain the spatial distribution as well as microscopic characteristics of corrosion products of the reinforcement bar under coupling conditions. Additionally, a model of steel rust cracking under the coupled action of chloride and fatigue loading is established. The results show that: under the same corrosion time, the concrete cracking and steel corrosion degree become more serious with the increase of stress level. The greater the stress level, the earlier corrosion occurs and the more corrosion products are, Moreover, due to the fatigue load, the concrete on the upper side of the steel bar has rust expansion cracks earlier than the lower side.


    Access

    Check access

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Corrosion Cracking Process of Reinforced Concrete under the Coupled Effects of Chloride and Fatigue Loading


    Additional title:

    KSCE J Civ Eng


    Contributors:
    Shen, Jiansheng (author) / Liu, Junzhe (author) / Xu, Yidong (author) / Jia, Kanghao (author) / Wu, Fangyu (author) / Chen, Wei (author) / Zhu, Dayong (author)

    Published in:

    Publication date :

    2021-09-01


    Size :

    14 pages




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    English




    Modeling of Chloride Ion Diffusion in Concrete under Fatigue Loading

    Yang, Tao / Guan, Bowen / Liu, Guoqiang et al. | Online Contents | 2019


    Modeling of Chloride Ion Diffusion in Concrete under Fatigue Loading

    Yang, Tao / Guan, Bowen / Liu, Guoqiang et al. | Springer Verlag | 2018


    Corrosion fatigue influence on gasket flange cracking

    Shuster,M. / Willis,H. / Dana,US | Automotive engineering | 1993


    Corrosion Fatigue Influence on Gasket Flange Cracking

    Willis, Harry / Shuster, Mark | SAE Technical Papers | 1993


    In Search of Rotorcraft Airframe Fatigue Assessment Methodology - Cracking Prediction under Service Loading

    Moon, S. / Phan, N. / American Helicopter Society | British Library Conference Proceedings | 2014