In this study, the fundamental and mineralogical properties of the binary system incorporating the industrial display byproducts, liquid crystal display (LCD) and organic light emitting diodes (OLED), as a cementitious material. A substitution level of the fine glass powders, and water to binder ratio were kept at 30% and 0.4 for all mixes, respectively. Strength development for the blended concretes was monitored until 91 days of curing, during which a modification of pore distribution was examined by mercury intrusion porosimetry. Simultaneously, the pozzolanic activity was evaluated by the content of calcium hydroxide (CH) in the cement pastes obtained from results of thermogravimetry analysis, and the phase composition of the specimens was quantitatively determined X-ray diffraction with Rietveld refinement method. As a result, the CH content in the glass-mixed specimen was decreased with time after certain age depending on glass types. Also, OLED was much effective to the pozzolanic activity, producing a higher content of C-S-H gel at 91 days, compared to LCD. This phenomenon may be attributed to a difference of Al2O3 and SiO2 content in the oxide composition, which would induce a shift of larger pore to micropore resulting in an increase in the strength for OLED concrete.


    Access

    Check access

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Strength Development Characteristics of Concrete Replaced with Different Waste Glasses from Display Industry as a Cementitious Material


    Additional title:

    KSCE J Civ Eng


    Contributors:

    Published in:

    Publication date :

    2020-08-01


    Size :

    10 pages




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    English




    Repair of Severely Damaged Reinforced Concrete Beams with High-Strength Cementitious Grout

    Gergess, Antoine N. / Shaikh Al Shabab, Mahfoud / Massouh, Razane | Transportation Research Record | 2020


    Low E Modulus Early Strength Engineered Cementitious Composites Material

    Zhang, Zhigang / Zhang, Qian / Qian, Shunzhi et al. | Transportation Research Record | 2015



    REPLACED ROLLER BEARING

    LINDBLEHJD STEFEN / FONTENOT UILL JAM / PRATT DZHEJMS NEL SON | European Patent Office | 2016

    Free access

    Delayed Strength Development of Composite Cementitious with Calcium Silicate Slag

    Bai, Ru / Zhang, Ju / Yan, Changwang et al. | Springer Verlag | 2023