Aluminum alloys have been replacing ferrous alloys in automotive applications to reduce the weight of vehicles. The engine block is a striking example of weight reduction, and is made of Al-Si-Cu-Mg (319 type) alloys. The wear resistance in the engine block is enabled by cast iron liners, and these liners introduce tensile residual stress due to a thermo-mechanical mismatch. Typically, an artificial aging treatment effectively reduces residual stress. In this study, neutron diffraction was used to measure the residual stress profiles along the cylinder bridge of a T5 treated 319 aluminum alloy engine block. Results indicated high tensile residual stresses (200-300 MPa) in the hoop and axial orientation at depths of 50-60 mm below the head deck. The high residual stresses were likely due to a combination of minimal stress relief during artificial aging and stress development during post process cooling.


    Access

    Check access

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Assessment of Residual Stress in T5 Treated 319 Aluminum Alloy Engine Blocks Using Neutron Diffraction


    Additional title:

    Sae Technical Papers


    Contributors:

    Conference:

    SAE 2016 World Congress and Exhibition ; 2016



    Publication date :

    2016-04-05




    Type of media :

    Conference paper


    Type of material :

    Print


    Language :

    English




    Assessment of Residual Stress in T5 Treated 319 Aluminum Alloy Engine Blocks Using Neutron Diffraction

    Ahmad, Suleman / Sediako, Dimitry / Lombardi, Anthony et al. | British Library Conference Proceedings | 2016


    Neutron Diffraction Study on Residual Stress in Aluminum Engine Blocks Following Machining and Service Testing

    Lombardy, A. / Sediako, D. / D Elia, F. et al. | British Library Conference Proceedings | 2012


    Neutron Diffraction Study on Residual Stress in Aluminum Engine Blocks Following Machining and Service Testing

    Lombardy, Anthony / Ravindran, C. (Ravi) / Sediako, Dimitry et al. | SAE Technical Papers | 2012


    Internal Residual Stress Measurement of Aluminum Alloy Castings Using Neutron Diffraction

    Kubota, Y. / Kubo, J. / Ishida, K. et al. | British Library Conference Proceedings | 2012


    Analysis of Residual Strain Profiles in Distorted Aluminum Engine Blocks by Neutron Diffraction

    Lombardi, A. / Ravindran, C. / Sediako, D. et al. | British Library Conference Proceedings | 2013