The fabrication or repairing of aircraft components made of Hastelloy X to be resolved using an arc welding technique. In this study, Hastelloy X was joint with ERNiCrCoMo-1 filler by pulsed current gas tungsten arc (PCGTA) welding. The high temperature tensile property of the weldment has been evaluated at three different temperatures such as 700 °C, 800 °C and 900 °C. The tensile properties such as yield strength (294, 259 and 205 MPa), ultimate tensile strength (475, 396 and 245 MPa) and percentage of elongation or ductility (17, 14 and 11 %) follows the similar trend with temperature at 700 °C, 800 °C and 900 °C respectively. It revealed the values of all the properties are decreased as the temperature increased. The lowest strength was evaluated for weldment at 900 °C. The high temperature tensile test also revealed that the fracture of weldments for all three conditions is found at the weld centre (WC). Even though, the failure happened at WC, the high temperature tensile strength of the weldments revealed that values are more or less equal to the base metal (Hastelloy X) values at 700 °C, 800 °C and 900 °C. The SEM fractography has been performed to find the tensile failure mode of weldments. The ductile dimples, ductile tear ridges and lesser cleavage-facet are found in the fractured region which derives the ductile failure.


    Access

    Check access

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Study on the High Temperature Tensile Properties of Aerospace Grade Hastelloy X Joined by Pulsed Current Arc Welding


    Additional title:

    Sae Technical Papers



    Conference:

    International Conference on Advances in Design, Materials, Manufacturing and Surface Engineering for Mobility ; 2020



    Publication date :

    2020-09-25




    Type of media :

    Conference paper


    Type of material :

    Print


    Language :

    English




    Study on the High Temperature Tensile Properties of Aerospace Grade Hastelloy X Joined by Pulsed Current Arc Welding

    Mathiyazhagan, Sathishkumar / Arivazhagan, Natarajan / Gokulkumar, Kesavan et al. | British Library Conference Proceedings | 2020


    Study on the High Temperature Tensile Properties of Aerospace Grade Hastelloy X Joined by Pulsed Current Arc Welding

    Mathiyazhagan, Sathishkumar / Arivazhagan, Natarajan / Gokulkumar, Kesavan et al. | British Library Conference Proceedings | 2020


    Hot Corrosion Demeanour of Key-Hole Plasma Arc Welded Aerospace Grade Hastelloy X in Molten Salts Environment

    Sathishkumar, Mathiyazhagan / Subramani, Pasupathi / Arivazhagan, Natarajan et al. | British Library Conference Proceedings | 2020


    Hot Corrosion Demeanour of Key-Hole Plasma Arc Welded Aerospace Grade Hastelloy X in Molten Salts Environment

    Sathishkumar, Mathiyazhagan / Subramani, Pasupathi / Arivazhagan, Natarajan et al. | British Library Conference Proceedings | 2020


    Hot Corrosion Demeanour of Key-Hole Plasma Arc Welded Aerospace Grade Hastelloy X in Molten Salts Environment

    Naiju, CD / GokulKumar, Kesavan / Manikandan, Manoharan et al. | SAE Technical Papers | 2020