Brønsted acidity of solution ion-exchanged and solid-state exchanged zeolites was compared for NaY, BaY, CaY, NaX, and CaX zeolites. These materials were chosen because they all exhibit catalytic activity in SCR of NOx in combination with a non-thermal plasma. Brønsted acidity was characterized qualitatively with retinol as an indicator dye. Our results show that the solid-state exchange using a chloride salt creates zeolites with lower acidity than zeolites obtained by conventional solution ion-exchange. NO2 adsorption was also found to create a significant quantity of acid sites at room temperature and a slight increase in acidity at 200°C. We speculate that the acid sites created by NO2 adsorption, because of their vicinity to metal cation sites in the zeolite, may lead to preferential reactions that lead to NOx reduction. BaY made by solution ion-exchange and BaY made by solid-state exchange using a chloride salt were tested for NOx reduction in a plasma-catalyst reactor system. Both catalysts showed similar catalytic activity. BaY prepared by solid-state exchange shows no coking due to absence of acid sites. In contrast, the BaY material prepared by conventional solution ion-exchange shows significant coke formation. Thus, the solid state exchanged BaY is a potentially more stable catalyst.


    Access

    Check access

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Characterization of Acid Sites in Ion-exchanged and Solid State-exchanged Zeolites


    Additional title:

    Sae Technical Papers


    Contributors:

    Conference:

    SAE International Fall Fuels & Lubricants Meeting & Exhibition ; 2001



    Publication date :

    2001-09-24




    Type of media :

    Conference paper


    Type of material :

    Print


    Language :

    English




    Characterization of acid sites in ion-exchanged and solid state-exchanged Zeolites

    Ebeling,A.C. / Panov,A.G. / McCready,D.E. et al. | Automotive engineering | 2001


    2001-01-3571 Characterization of Acid Sites in Ion-exchanged and Solid State-exchanged Zeolites

    Ebeling, A. C. / Panov, A. G. / McCready, D. E. et al. | British Library Conference Proceedings | 2001




    Catalytic Reduction of S. I. Engine Emissions Using Ion-Exchanged X-Zeolites

    Ghosh, B. B. / Das, Randip K. | SAE Technical Papers | 1999