The objective of this research was to determine fatigue behavior of SAE 1045 steel subjected to very high tensile mean stress for unnotched, mildly notched, and sharply notched test specimens, and to determine if common S-Nf and ε-Nf mean stress fatigue life models are applicable. High tensile mean stress fatigue tests for R ratios of 0.8 and 0.9 were conducted using unnotched and notched, Kt=1.65 and Kt=3.65, axial loaded SAE 1045 steel specimens with hardness levels of Rc=10, 37, and 50. The monotonic notch strength ratio, NSR, for 5 of 6 test conditions was greater than 1, which allowed many notched cyclic test values of Smax or Sm to exceed the unnotched ultimate tensile strength. Much notched specimen fatigue resistance at these high R ratios was superior to that of unnotched specimens. However, cyclic creep/ratcheting, particularly for Rc=10 and 37, was a predominant cause of failure. Scanning electron microscopy examination revealed many cyclic failures were similar to monotonic failures consistent with cyclic creep/ratcheting measurements. Specimens failed due to cyclic creep/ratcheting, to an interaction between cyclic creep/ratcheting and fatigue, or to surface fatigue crack nucleation and growth only. Fatigue life calculations based on S-Nf and ε-Nf models were up to 5 orders of magnitude in error, and thus completely unreasonable at these high R ratios. For a given test condition, this inaccuracy was due to cyclic creep/ratcheting, scatter, notch strengthening, material properties used, inherent inaccuracy of S-Nf constant life diagrams at high R ratios, and/or extrapolation of the Ramberg-Osgood equation beyond Su and σf.


    Access

    Check access

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    The Effect of High Tensile Mean Stress on Fatigue of Unnotched and Notched SAE 1045 Steel


    Additional title:

    Sae Technical Papers


    Contributors:

    Conference:

    SAE 2003 World Congress & Exhibition ; 2003



    Publication date :

    2003-03-03




    Type of media :

    Conference paper


    Type of material :

    Print


    Language :

    English




    The Effect of High Tensile Mean Stress on Fatigue of Unnotched and Notched SAE 1045 Steel

    Stephens, R. I. / Pals, T. J. / Karadag, M. et al. | British Library Conference Proceedings | 2003


    Tensile behavior of unnotched and notched tungsten-copper laminar composites

    Hoffman, Charles A. / Weeton, John W. | TIBKAT | 1976