100 kHz core loss properties of sample transverse magnetically annealed, cobalt-based amorphous and iron-based nanocrystalline tape wound magnetic cores are presented over the temperature range of -150 C to 150 C, at selected values of Bpeak. For B-fields not close to saturation, the core loss is not sensitive to temperature in this range and is as low as seen in the best MnZn power ferrites at their optimum temperatures. Frequency resolved characteristics are given over the range of 50 kHz to 1 MHz, but at Bpeak = 0.1 T and 50 C only. For example, the 100 kHz specific core loss ranged from 50 mW/cm3 to 70 mW/cm3 for the 3 materials, when measured at 0.1 T and 50 C. This very low high frequency core loss, together with near zero saturation magnetostriction and insensitivity to rough handling, makes these amorphous ribbons strong candidates for power magnetics applications in wide temperature aerospace environments


    Access

    Check access

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Wide Temperature Core Loss Characteristics of Transverse Magnetically Annealed Amorphous Tapes for High Frequency Aerospace Magnetics


    Additional title:

    Sae Technical Papers


    Contributors:

    Conference:

    34th Intersociety Energy Conversion Engineering Conference ; 1999



    Publication date :

    1999-08-02




    Type of media :

    Conference paper


    Type of material :

    Print


    Language :

    English





    High Temperature Magnetics for Power Conversion

    A. Brockschmidt / I. Mehdi | NTIS | 2005



    Magnetics research at nasa

    Callaghan, E. E. | NTRS | 1961


    Wide-temperature-zone temperature control system of aerospace ring die equipment

    WANG XIAOZHAN / LIU JIALIN / GUAN YANG et al. | European Patent Office | 2021

    Free access