Cd,Zn)S buffer layer and Zn 1− x Mg x O window layer were investigated to replace the traditional CdS buffer layer and ZnO window layer in Cu(In,Ga)(Se,S) 2 (CIGSSe)‐based solar cell. (Cd,Zn)S with band‐gap energy ( E g ) of approximately 2.6 eV was prepared by chemical bath deposition, and Zn 1− x Mg x O films with different [Mg]/([Mg] + [Zn]) ratios, x , were deposited by radio frequency magnetron co‐sputtering of ZnO and MgO. The estimated optical E g of Zn 1− x Mg x O films is linearly enhanced from 3.3 eV for pure ZnO ( x = 0) to 4.1 eV for Zn 0.6 Mg 0.4 O ( x = 0.4). The quality of the Zn 1− x Mg x O films, implied by Urbach energy, is severely deteriorated when x is above 0.211. Moreover, the temperature‐dependent current density‐voltage characteristics of the CIGSSe solar cells were conducted for the investigation of the heterointerface recombination mechanism. The external quantum efficiency of the CIGSSe solar cell with the (Cd,Zn)S buffer layer/Zn 1− x Mg x O window layer is improved in the wavelength range of 320–520 nm. Therefore, a gain in short‐circuit current density up to about 5.7% was obtained, which is higher conversion efficiency of up to around 5.4% relative as compared with the solar cell with the traditional CdS buffer layer/ZnO window layer. The peak efficiency of 19.6% was demonstrated in CIGSSe solar cell with (Cd,Zn)S buffer layer and Zn 1− x Mg x O window layer, where x is optimized at 0.211. Copyright © 2017 John Wiley & Sons, Ltd. The traditional CdS buffer layer and ZnO window layer are replaced by (Cd,Zn)S buffer layer and Zn 1− x Mg x O window layer in Cu(In,Ga)(Se,S)2 (CIGSSe)‐based solar cell. External quantum efficiency of the CIGSSe solar cell with the (Cd,Zn)S buffer layer and Zn 1− x Mg x O window layer is improved in the wavelength range of 320–520 nm. Efficiency of 19.6% is ultimately demonstrated in CIGSSe solar cell with (Cd,Zn)S buffer layer and Zn 1− x Mg x O window layer, where x is optimized at 0.211.
Thin‐film Cu(In,Ga)(Se,S)2‐based solar cell with (Cd,Zn)S buffer layer and Zn1−xMgxO window layer
Progress in photovoltaics ; 25 , 6
2017
Article (Journal)
English
BKL: | 53.36 Energiedirektumwandler, elektrische Energiespeicher |
Atomic layer deposition of Zn1-xMgxO buffer layers for Cu(In,Ga)Se2 solar cells
Online Contents | 2007
|CdTe thin film solar cell with NiO as a back contact buffer layer
Online Contents | 2017
|Synthesis and Characterization of Zn1-xMgxO Thin Films
AIAA | 2006
|Thin-film ZnO/Cu2O solar cells incorporating an organic buffer layer
Online Contents | 2012
|