Minimum weight configurations for two types of graphite-epoxy hat-stiffened compression-loaded panels fabricated by the thermal-expansion-molding (TEM) manufacturing process were evaluated analytically and experimentally for designs with load index Nx/L values ranging from 100 to 800. The two types of panels contain graphite-epoxy face sheets with a foam core and hat stiffeners which are either open or filled with foam. Constraints on the extensional and shear stiffnesses are imposed on the design so that the panels will satisfy typical constraints for aircraft wing structures. Optimal structurally efficient TEM panels are compared to commercially available aluminum aircraft structures. Predicted load-strain relationships agree well with experimental results. Significant impact damage to the unstiffened face sheet and foam core does not noticeably reduce the load carrying ability of the panels, but damage to the stiffened face sheet reduces the failure load by 20 percent compared to unimpacted panels.
Design and testing of thermal-expansion-molded graphite-epoxy hat-stiffened sandwich panels
AIAA, ASME, ASCE, AHS, and ASC, Structures, Structural Dynamics and Materials Conference ; 1989 ; Mobile, AL, United States
1989-01-01
Conference paper
No indication
English
Study of thermal-expansion-molded, graphite-epoxy hat-stiffened sandwich panels
Tema Archive | 1991
|