Use of time-to-failure curves for stress-corrosion cracking processes may lead to incorrect estimates of structural life, if material is strongly dependent upon prestress levels. Technique characterizes kinetics of crackgrowth rates and intermediate arrest times by load-level changes.
Kinetic studies of stress-corrosion cracking
NASA Tech Briefs ; 2 , 3