Stress corrosion cracking susceptability in presence of hydrazine is examined for 6061-T6, Ti-6A1-4V(STA), Inconel 718, 410 stainless steel, and 4130 steel alloys.


    Access

    Access via TIB

    Check availability in my library


    Export, share and cite



    Title :

    Stress-corrosion cracking due to hydrazine


    Contributors: