The invention discloses a bainite non-quenched and tempered steel material, a steering knuckle and a preparation method, relates to the technical field of non-quenched and tempered steel materials, and further improves the obdurability of automobile steering knuckles. The material comprises the following components in percentage by weight: 0.33 percent to 0.37 percent of C, 0.15 percent to 0.35 percent of Si, 1.9 percent to 2.05 percent of Mn, less than or equal to 0.03 percent of P, 0.04 percent to 0.07 percent of S, 0.20 percent to 0.50 percent of Cr and 0.20 percent to 0.30 percent of V. The preparation process comprises the following steps: S1, electric furnace smelting; s2, LF refining; s3, VD vacuum treatment; S4, ingot casting; s5, heat treatment; s6, rolling is conducted; s7, air cooling; s8, finishing is conducted; and S9, flaw detection. The preparation method of the steering knuckle comprises the following steps: T1, blanking; t2, induction heating; t3, primary forging; t4, intermediate forging is conducted; t5, finish forging; t6, trimming is conducted; and T7, fan forced cooling.
一种贝氏体非调质钢材料、转向节以及制备方法,涉及非调制钢材料技术领域,进一步提升了汽车转向节的强韧性。所述材料包含按重量百分比计的以下组分:C:0.33%~0.37%,Si:0.15%~0.35%,Mn:1.9%~2.05%,P≤0.03%,S:0.04%~0.07%,Cr:0.20%~0.50%,V:0.20%~0.30%。制备工艺包括:S1、电炉冶炼;S2、LF精炼;S3、VD真空处理S4、铸锭;S5、热处理;S6、轧制;S7、空冷;S8、精整;S9、探伤。转向节制备方法包括:T1、下料;T2、感应加热;T3、初锻;T4、中锻;T5、终锻;T6、切边;T7、风扇强制冷却。
Bainite non-quenched and tempered steel material, steering knuckle and preparation method
一种贝氏体非调质钢材料、转向节以及制备方法
2023-03-07
Patent
Electronic Resource
Chinese
European Patent Office | 2023
|European Patent Office | 2022
|