HighlightsVacuum sealing capability of elastomeric O-rings is tested for in situ K–Ar dating.Argon blanks are measured and compared with signals from potential targets.Viton O-rings achieve the blank-to-signal ratio of <1% under Martian air pressure.A double O-ring seal with cold-resistant elastomers will achieve blank/signal <1%.
AbstractMass spectrometry has been widely used in lander missions to characterize the volatiles in rocks and soils on planetary surfaces. A good vacuum seal is very important for introducing such solid samples to a vacuum chamber and ejecting them. However, multiple measurements require many metal gaskets, leading to extra weight and complexity for the instruments. In this study, we investigate the capability of three kinds of elastomeric O-rings (Viton, Nexus-SLT, and Nexus-FV) as vacuum seals for mass spectrometric measurements, particularly for in situ K–Ar dating on Mars. First, thermal cycle tests revealed that low-temperature-resistant O-rings can maintain pressure <10−5Pa at −60°C under 1bar ambient pressure, whereas Viton O-rings leaked at −25°C. Then, the amount of 40Ar due to outgassing from the O-rings and permeation under the ambient pressure of 650Pa or 3Pa was measured and compared with the amounts of 40Ar that a flight-equivalent laser would liberate from potential target Martian rocks. The measured amounts were <1% of that a target rock with 5000ppm K2O and an age of 4.2Ga would yield. These results suggest that a Viton O-ring can maintain the Ar blank low under the Mars atmospheric pressure when temperatures are higher than −25°C. A double O-ring seal using the low-temperature-resistant elastomers would be an alternative approach at lower temperatures. The elastomeric O-rings would be useful for constructing a small and light-weighted mass spectrometric instrument for in situ K–Ar dating on Mars.
Experimental characterization of elastomeric O-rings as reusable seals for mass spectrometric measurements: Application to in situ K–Ar dating on Mars
Advances in Space Research ; 60 , 7 ; 1453-1462
2017-07-02
10 pages
Article (Journal)
Electronic Resource
English
Gland Design, Elastomeric O-Ring Seals, Static Axial, Without Backup Rings
SAE Technical Papers | 1995
Gland Design, Elastomeric O-Ring Seals, Static Axial, Without Back-Up Rings
SAE Technical Papers | 2012
Elastomeric seals in hard vacuum
AIAA | 1964
|SOUND TRANSMISSION THROUGH ELASTOMERIC BULB SEALS
Online Contents | 2003
|