Ni-Cr-B brazing filler was used to braze FGH96 and DD6 at 1120℃/10 min and 1120℃/10 min/2 MPa. The tensile strength of the joints was tested, the microstructures and fractures were observed by OM and SEM, and the reaction products were analyzed by EPMA. The results show that the joints brazed at vacuum pressure process offer the average tensile strength of 1187 MPa, outclass the joints brazed without pressure which has average tensile strength of 621 MPa. Compared with vacuum brazing, the grains of FGH96/DD6 joints brazed by vacuum pressure state penetrate the brazing seam without grain boundary and ductile fracture occurred in the parent metal surface. The Ni3B exists in the joints brazed by vacuum brazing, but it is (Ni, Cr) solid solution in the joints brazed by vacuum pressure brazing instead of Ni3B.


    Access

    Download


    Export, share and cite



    Title :

    Microstructures and Properties of FGH96/DD6 Joints Brazed at Vacuum Pressure State


    Contributors:
    ZOU Wenjiang (author) / CHEN Bo (author) / CHENG Yaoyong (author) / MAO Wei (author) / XIONG Huaping (author)


    Publication date :

    2017




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    Unknown




    Brazed Pipe Joints

    Duckworth, D.J. | Emerald Group Publishing | 1964



    Clad metals provide better brazed joints

    Dibble,M. A. | Automotive engineering | 1993


    The nondestructive testing of brazed joints

    Kannō, Akira | TIBKAT | 1964