The microstructural and crystallographic features of the surface deformation layer in Al-Zn-Mg-Cu alloy induced by milling were investigated by means of transmission electron microscopy (TEM) and precession electron diffraction (PED) assisted nanoscale orientation mapping. The result shows that the surface deformation layer is composed by the top surface of equiaxed nanograins/ultrafine grains and the subsurface of lamellar nanograins/ultrafine grains surrounded by coarse grain boundary precipitates (GBPs). The recrystallized nanograins/ultrafine grains in the deformation layer show direct evidence that dynamic recrystallization plays an important role in grain refining process. The GBPs and grain interior precipitates (GIPs) show a great difference in size and density with the matrix due to the thermally and mechanically induced precipitate redistribution. The crystallographic texture of the surface deformation layer is proved to be a mixture of approximate copper{112}<111>, rotated cube{001}<110> and F {111}<112>. The severe shear deformation of the surface induced by milling is responsible for the texture evolution.
Microstructure and Texture in Surface Deformation Layer of Al-Zn-Mg-Cu Alloy Processed by Milling
2017
Article (Journal)
Electronic Resource
Unknown
Metadata by DOAJ is licensed under CC BY-SA 1.0
Effect of High-Speed Milling Parameters on Surface Metamorphic Layer of TC17 Titanium Alloy
DOAJ | 2017
|Surface Texture and Microstructure Extraction from Multiple Aerial Images
British Library Online Contents | 2001
|Deformation and Texture Behaviors of Al-3mass%Mg Alloy at High Temperatures
SAE Technical Papers | 2003
|Relationship between Microstructure and Deformation Behavior of Fe~3Al Alloy
British Library Conference Proceedings | 1993
|