Graphene oxide (GO) modified epoxy resin (GH81) was prepared by mechanical grinding, and the dispersion of GO in the epoxy resin (H81) was analyzed by optical microscope, while the melting performances and curing behaviors of H81 and GH81 were researched through rheometer and differential scanning calorimeter respectively. The results show that GO is uniformly dispersed into the matrix resin,and the addition of GO hardly affects the melt viscosity and curing condition of the matrix resin at all. In addition, the 0° tensile strength, bending strength and compression strength of GH81 based carbon fiber reinforced composite (GH81-300) are 2270 MPa, 2239 MPa and 1529 MPa respectively, which is increased by 6.4%, 7.2% and 7.1% respectively, as compared with that of composite without GO.


    Access

    Download


    Export, share and cite



    Title :

    Properties of graphene oxide modified epoxy resin and its composites


    Contributors:
    REN Zhidong (author) / HAO Sijia (author) / XING Yue (author) / YANG Cheng (author) / DAI Shenglong (author)


    Publication date :

    2019




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    Unknown




    Mechanical and thermal properties of epoxy composites containing graphene oxide and liquid crystalline epoxy

    Qi, B. / Yuan, Z. / Lu, S. et al. | British Library Online Contents | 2014


    Fluorophlogopite-Filled Epoxy Resin Composites

    Yonghong, Z. / Xiangling, L. / Guangxin, L. | British Library Online Contents | 2002


    Enhanced thermal properties for epoxy composites with a three-dimensional graphene oxide filler

    Gao, J. / Yu, J. / Wu, X. et al. | British Library Online Contents | 2015


    Epoxy-modified cyanate ester resin and its high-modulus carbon-fiber composites

    Ren, Penggang / Liang, Guozheng / Zhang, Zengping | Tema Archive | 2006


    Nanomaterial modified fusion bonded epoxy resin and its properties

    LIU Fuxin / DU Juan | DOAJ | 2025

    Free access