In order to obtain a large modified zone with uniform microstructure and good comprehensive properties, single-side and double-side friction stir processings of Mg-Zn-Y-Nd alloy thick plate were carried out, and the microstructure and properties of the processed plates were studied. The results show that the microstructure of the alloy is obviously refined after friction stir processing. The average grain sizes of the upper, mid and lower samples in the stirring zone after single-side and double-side friction stir processings are 4.45 μm, 5.08 μm,5.30 μm and 3.93 μm, 3.20 μm and 3.19 μm respectively. Compared with the homogenizing annealing alloy and single-side friction stir processed alloy, the microstructure of the double-side friction stir processed alloy is more uniform and fine, and the tensile strength and elongation of the lower stirring zone are the highest, 283.3 MPa and 23.9% respectively, and also the corrosion resistance is the best. The corrosion mode is changed from pitting corrosion to uniform corrosion.


    Access

    Download


    Export, share and cite



    Title :

    Effects of single-side and double-side friction stir processing on microstructure and properties of Mg-Zn-Y-Nd alloy thick plate


    Contributors:
    XU Xuexue (author) / ZHU Shijie (author) / WANG Qing (author) / WANG Liguo (author) / SUN Yufeng (author) / GUAN Shaokang (author)


    Publication date :

    2019




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    Unknown




    Friction stir welding aluminum alloy side wall profile and application thereof

    WANG MINGKUN / SUN WENCHAO / WANG TAO et al. | European Patent Office | 2023

    Free access

    Friction stir welding aluminum alloy ship bottom plate

    SUN YINGJIE / CUI GUOCHANG | European Patent Office | 2022

    Free access

    Microstructure and properties of 2219 aluminum alloy fabricated via additive friction stir deposition

    WANG Ruilin / YANG Xinqi / TANG Wenshen et al. | DOAJ | 2024

    Free access


    Effects of friction stir processing on mechanical properties of the cast aluminum alloy a356

    Santella,M.L. / Engstrom,T. / Storjohann,D. et al. | Automotive engineering | 2005