There is a problem about microstructure evolution and properties degradation for the superalloy turbine blades in long term service conditions. DZ406 alloy samples were pre-loaded to simulate the high temperature service environment of turbine blades. The thermodynamic coupling simulation conditions were 980 ℃/70 MPa, 980 ℃/110 MPa, 980 ℃/140 MPa and 980 ℃/180 MPa respectively. And then the samples were subjected to stress rupture property test at 980 ℃/275 MPa. The microstructure and 980 ℃/275 MPa rupture life of the samples under different service loading conditions were observed and analyzed. The results show that the heat treatment microstructure of DZ406 alloy is composed of carbides, residual γ +γ´ eutectic and regular γ´ phase. The morphology and size of carbides and eutectic have no obvious change with the increase of loading stress under simulated service conditions. The γ´ phase of the sample parallel to [001] direction presents different degrees of rafting, and the size of γ´ phase perpendicular to [001] direction obviously increases. The residual stress rupture life of the sample declines rapidly with the increase of service stress.


    Access

    Download


    Export, share and cite



    Title :

    Effect of thermodynamic coupled simulation condition on microstructure and stress rupture properties of DZ406 alloy


    Contributors:
    JIA Xinyun (author) / ZONG Cui (author) / GUO Jing (author) / CHEN Shengping (author) / ZHENG Zhen (author) / ZHAO Wenxia (author) / HUANG Zhaohui (author)


    Publication date :

    2022




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    Unknown




    Effect of heat treatment on intermediate temperature stress rupture properties of alloy K403

    Zheng, Y. / Li, S. / Ma, S. | British Library Online Contents | 1997


    Influence of Aging Temperature on the Microstructure and Stress Rupture Property of DZ951 Alloy

    Xia, P. C. / Yu, J. J. / Sun, X. F. et al. | British Library Conference Proceedings | 2007


    Effect of Co content on microstructure and stress rupture properties of DD15 single crystal superalloy

    SHI Zhenxue / LIU Shizhong / YUE Xiaodai et al. | DOAJ | 2020

    Free access