7% yttria stabilized zirconia (7YSZ) thermal barrier coatings (TBCs) prepared by air plasma spray were laser-remelted, and subsequently pre-heated and Al2O3 sol-gel repaired for restraining the crack growth in the remelted coatings. The as-prepared coatings were exposed to high temperature molten CaO-MgO-Al2O3-SiO2 (CMAS) to explore their corrosion resistance. The results show that both the laser remelted and the pre-heated, the laser-remelted coatings are densified by CMAS attack. In addition, the thickness of the densified layers is on the same order of that of the non-remelted coatings. Despite of this, the densified layer in the laser remelted coating repaired by Al2O3 sol-gel is much thinner than the other coatings. This indicates that Al2O3 sol-gel repairing coupling with laser-remelted method can effectively improve the CMAS resistance of 7YSZ TBCs due to the refractory anorthite generated during corrosion process. This refractory compound produced between CMAS and Al2O3 sol-gel is capable to decrease the mobility and corrosivity of the CMAS.


    Access

    Download


    Export, share and cite



    Title :

    Improving molten CMAS resistance of thermal barrier coatings by modified laser remelting method


    Contributors:
    ZHAO Changhao (author) / YANG Lingwei (author) / XIAO Xueren (author) / ZHANG Jun (author) / PAN Wei (author)


    Publication date :

    2022




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    Unknown




    Degradation of Thermal Barrier Coatings by Molten CMAS (CaO-MgO-Al2O3-SiO2) Deposits

    Mohan, Prabhakar / Desai, Vimalkumar / Sohn, Yongho et al. | AIAA | 2009


    Effect of yttria content on CMAS resistance of YSZ thermal barrier coatings

    WANG Jing / LU Jie / ZHAO Xiaofeng et al. | DOAJ | 2023

    Free access

    Degradation of Thermal Barrier Coatings by Molten CMAS (CaO-MgO-Al~2O~3-SiO~2) Deposits

    Mohan, P. / Desai, V. / Sohn, Y. et al. | British Library Conference Proceedings | 2009



    Failure and Protection of Thermal Barrier Coating under CMAS Attack

    YANG Shanjie / PENG Hui / GUO Hongbo | DOAJ | 2018

    Free access