This paper describes the development of a novel technique to understand the failure mechanisms inside thermal protection materials. The focus of this research is on the class of materials known as phenolic impregnated carbon ablators. It has successfully flown on the Stardust spacecraft and is the thermal protection system material chosen for the Mars Science Laboratory and SpaceX Dragon spacecraft. Although it has good thermal properties, structurally, it is a weak material. To understand failure mechanisms in carbon ablators, fracture tests were performed on FiberForm®§ (precursor), virgin, and charred ablator materials. Several samples of these materials were tested to investigate failure mechanisms at a microstructural scale. Stress-strain data were obtained simultaneously to estimate the tensile strength and toughness. It was observed that cracks initiated and grew in the FiberForm when a critical stress limit was reached such that the carbon fibers separated from the binder. However, both for virgin and charred carbon ablators, crack initiation and growth occurred in the matrix (phenolic) phase. Both virgin and charred carbon ablators showed greater strength values compared with FiberForm samples, confirming that the presence of the porous matrix helps in absorbing the fracture energy.
Fracture in Phenolic Impregnated Carbon Ablator
Journal of Spacecraft and Rockets ; 50 , 4 ; 735-741
2013-06-05
7 pages
Article (Journal)
Electronic Resource
English
Fracture in Phenolic Impregnated Carbon Ablator
Online Contents | 2013
|Fracture in Phenolic Impregnated Carbon Ablator
AIAA | 2011
|Nonequilibrium Ablation of Phenolic Impregnated Carbon Ablator
Online Contents | 2012
|NON-EQUILIBRIUM ABLATION OF PHENOLIC IMPREGNATED CARBON ABLATOR
British Library Conference Proceedings | 2010
|