This paper presents results from a study where the corrosion performance of plain C-Mn steel and low alloyed (0.5 % Cr) steel was compared in different types of brines at 82 deg C, 0.5 bar CO2 and a flow velocity of 2.3 m/s. Inhibitor efficiencies to be expected in the different brines and necessary inhibitor concentration for satisfactory corrosion protection are investigated. The build up of protective corrosion product films on 0.5 % Cr-steel is dependent on the corrosivity of the brine. In high corroding brines, the protective films are built up within days, but in low corrosive brines and inhibited brines the film formation is slow. As a result the positive effect of chromium alloying will not be revealed during short time testing. The natural formation water used in the presented tests is much less corrosive than the substitute brines. However, the corrosion rate after inhibitor injection seems to be unaffected of the initial corrosion rate, and far lower inhibitor efficiencies are therefore recorded in the natural formation water.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Corrosion of C-Mn-steel and 0.5 % Cr steel in flowing CO2 saturated brines


    Weitere Titelangaben:

    Korrosion von C-Mn-Stahl und Chromstahl bei Durchströmung mit CO2-gesättigter Sole


    Beteiligte:
    Rogne, T. (Autor:in) / Eggen, T.G. (Autor:in) / Steinsmo, U. (Autor:in)


    Erscheinungsdatum :

    1996


    Format / Umfang :

    14 Seiten, 10 Bilder, 2 Tabellen, 7 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Inhibition of weld corrosion in flowing brines containing carbon dioxide

    Alawadhi, K. / Robinson, M. / Chalmers, A. et al. | Tema Archiv | 2008



    Corrosion of mild steel in different granularity seabed sediment saturated with seawater

    Jizhou, D. / Hou, Baorong / Yanliang, H. et al. | Tema Archiv | 2002


    Corrosion and control of P110 oil tube steel in CO2-saturated solution

    Zhao, J.M. / Lu, Y. / Liu, H.X. | Tema Archiv | 2008