This short communication serves to report the results of fatigue testing which was conducted on single-edge-notched rectangular bar specimens machined from the head of a length of virgin head-hardened heavy haul railway rail, manufactured using an ingot route. An increasing load technique was employed for threshold determination with small positive stress ratio R. The tests resulted in a fatigue threshold of 11.4+/-0.4 MPa m1/2 for R = 0.11. This is slightly lower than the established fatigue threshold for standard carbon raid steel of 12-14 MPa m1/2.
Mode I fatigue threshold for head hardened rail steel
International Journal of Fatigue ; 20 , 3 ; 247-249
1998
3 Seiten, 8 Quellen
Aufsatz (Zeitschrift)
Englisch
Investigation of rolling contact fatigue in a head-hardened rail
Tema Archiv | 1991
|Rail steels - Head-hardened rail put to the test
Online Contents | 2004
The Head Hardened Rail - is it economical?
British Library Conference Proceedings | 1999
|Rail steels Head-hardened rail put to the test
British Library Online Contents | 2004
Head-hardened rail put to the test
IuD Bahn | 2004
|