A hot-dip coated stainless steel sheet has been newly developed as a material with excellent corrosion resistance in a severe marine environment. From the results of exposure test in this environment, inducing red-rusting to a type 304 bare stainless steel sheet, it was concluded that an Al coated type 430 stainless steel sheet has kept the initial surface appearance and had no red-rust even on the bare surface of base steel at cut edges and cross-scribes. This was confirmed by electrochemical investigation that a sacrificial corrosion of the Al coating and alloy layer protected effectively the bare surface of base stainless steel.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Corrosion resistance of aluminium coated stainless steel sheet under marine environment


    Weitere Titelangaben:

    Korrosionsbeständigkeit von aluminiumbeschichtetem nichtrostendem Stahlblech unter marinen Bedingungen


    Beteiligte:
    Hatanaka, N. (Autor:in) / Hattori, Y. (Autor:in) / Miyoshi, Y. (Autor:in) / Uchido, Y. (Autor:in) / Hirose, Y. (Autor:in)


    Erscheinungsdatum :

    1989


    Format / Umfang :

    8 Seiten, 6 Bilder, 2 Tabellen, 4 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Undervehicle corrosion resistance of 55 % Al-Zn coated steel sheet

    Allegra, L. / Townsend, H.E. | Tema Archiv | 1981


    Marine Exposure Tests on Stainless Steel Sheet

    Mitchler, Willard | NTRS | 1947




    Corrosion behavior of organic composite coated steel sheet

    Sujita,S. / Muko,R. / Mochizuki,K. et al. | Kraftfahrwesen | 1993